Permana, Sulaksana and Rachel, Debby and Prasetyo, Agus Budi and Majid, Rafdi Abdul and Kartika, Wahyu and Susanto, Iwan and Soedarsono, Johny Wahyuadi (2020) PENGKAYAAN UNSUR YTTRIUM DAN CERIUM PADA TERAK TIMAH BANGKA: ANALISIS TERMODINAMIKA. Pusat Penelitian Metalurgi dan Material – LIPI, Indonesia.

This is the latest version of this item.

Full text not available from this repository.
Official URL: http://www.ejurnalmaterialmetalurgi.com

Abstract

Abstrak Pada penelitian ini, terak timah Bangka-2 (TTB-2) dilakukan serangkaian kondisi proses untuk mendapatkan hasil pengkayaan yttrium dan cerium yang optimal. Proses yang dilakukan adalah dengan melakukan pemanggangan TTB-2 pada suhu 900 °C, pelindian dengan NaOH, pelindian dengan HNO3 dan terakhir pelindian dengan H3PO4 dengan variasi konsentrasi. Analisis termodinamika dilakukan dengan perangkat lunak HSC 6.0 untuk mendapatkan Diagram Eh-pH sistem Ca-Na-H2O; Ce-Na-H2O; Y-Na-H2O; Ce-N-H2O; Y-N-H2O; Ce-P-H2O dan Y-P-H2O pada suhu 25 °C dengan tujuan melihat unsur yang terlarut ke dalam larutan NaOH, HNO3 dan H3PO4. Hasil yang didapatkan adalah kadar optimal cerium 4,39% setelah kondisi proses pelindian NaOH dan kadar yttrium mengalami peningkatan terus pada seluruh kondisi proses serta didapatkan kadar optimal 1,35% setelah dilakukan pelindian dengan HNO3 2M dan H3PO4 1,5 M. Kata Kunci: Cerium, pelindian, terak timah Bangka, unsur tanah jarang, yttrium Abstract In this analysis, the Bangka tin slag-2 (BTS-2) was carried out in a series of process conditions to obtain optimal yttrium and cerium enrichment results. The method is carried out by roasting BTS-2 at 900 °C, leaching with NaOH, leaching with HNO3, and finally leaching with H3PO4 with different concentrations. The thermodynamic analysis was performed using HSC 6.0 software to obtain the Ca-Na-H2O Eh-pH diagram system; Ce-Na-H2O; YNa-H2O; Ce-N-H2O; Y-N-H2O; Ce-P-H2O and Y-P-H2O at 25 °C to see the leached elements in NaOH, HNO3, and H3PO4 solutions. The results obtained were that the optimal cerium content was 4.39 % after the NaOH leaching phase. The yttrium content continued to increase under all process conditions, and that the optimal cerium content was 1.35 % after leaching with HNO3 2 M and H3PO4 1.5 M. Keywords: Cerium, leaching, Bangka tin slag, rare earth element, yttrium

Item Type: Other
Subjects: Teknologi dan Ilmu Terapan > Teknik Lingkungan
Divisions: Fakultas Teknik > Teknik Lingkungan
Depositing User: Wahyu Kartika
Date Deposited: 22 Jun 2022 03:06
Last Modified: 22 Jun 2022 03:06
URI: http://repository.ubharajaya.ac.id/id/eprint/14265

Available Versions of this Item

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year