Abdul Majid, Rafdi and Permana, S and Soedarsono, J,W and Rachel, Debby and Kartika, Wahyu and Darnengsih, D and Munira, Munira and Mustafiah, M (2019) Peningkatan Kadar Tantalum & Niobium Oksida dari Terak Timah Bangka Menggunakan Pelarut NaOH dilanjutkan dengan HNO3 dan H3PO4. Department of Chemical Engineering Faculty of Industrial Technology Universitas Muslim Indonesia, Makassar, Indonesia.

Text Peer Review Peningkatan Kadar Tantalum.pdf Download (553kB)

Abstract

Inti Sari Terak Timah merupakan produk samping dari proses peleburan timah yang mengandung unsur logam tantalum dan niobium. Beberapa sumber unsur tantalum dan niobium yaitu columbite, tantalite, tantalo-columbite, dll. Tantalum & niobium memiliki banyak aplikasi seperti industri pesawat terbang, elektronik dan super alloy. Penelitian ini dilakukan untuk meningkatkan kadar unsur logam tantalum dan niobium dari terak timah melalui proses pelindian asam maupun basa. Hasil penelitian menunjukan bahwa proses pemanggangan yang dilakukan tidak mengalami dekomposisi thermal, selanjutnya proses pelindian basa dengan NaOH mengakibatkan penurunan yang sangat kecil terhadap niobium yaitu dari 0,75 menjadi 0,73%, sedangkan proses pelindian dengan HNO3 dan H3PO4 memberikan peningkatan terhadap tantalum dan niobium yaitu dengan HNO3 2M menghasilkan Ta dan Nb berturut-turut 0,17 menjadi 0,85 dan 0,73 menjadi 1,49. Hal ini juga terlihat pada pelindian menggunakan campuran HNO3: H3PO4 menghasilkan peningkatan Ta dan Nb berturut-turut menjadi 0,88-0,9% dan 1,46-1,54% di setiap peningkatan variasi konsentrasi H3PO4. Kata Kunci: Terak Timah Bangka, Tantalum, Niobium, Pelindian, Pemanggangan Abstract Tin slag is a by-product of tin processing that have tantalum and niobium contents. Some source of tantalum and niobium is columbite, tantalite, etc, with many applications likes aircraft industry, electronics, super alloy. In this study, we will increase the contents of tantalum and niobium from tin slag by process of alkaline and acid leaching. The results showed that roasting process carried out didn’t cause thermal decomposition, then process of alkaline leaching by NaOH tend to very small decrease of niobium oxide from 0,75% to 0,73%. Which the process of acid leaching by HNO3 and H3PO4 given increases to tantalum and niobium oxides, while the leaching process with HNO3 and H3PO4 gives an increase of tantalum and niobium, with 2M HNO3 producing Ta and Nb, respectively 0.17 to 0.85 and 0.73 to 1.49. This is also seen in leaching with a mixture of HNO3: H3PO4 resulting in an increase of Ta and Nb respectively to 0.88-0.9% and 1.46-1.54% in each variation of H3PO4 concentration. Key Words : Bangka Tin Slag,Tantalum, Niobium, Leaching, Roasting

Item Type:	Other
Subjects:	Teknologi dan Ilmu Terapan > Teknik Lingkungan Teknologi dan Ilmu Terapan > Teknik Kimia
Divisions:	Fakultas Teknik > Teknik Kimia
Depositing User:	Wahyu Kartika
Date Deposited:	14 Feb 2022 03:02
Last Modified:	14 Feb 2022 03:02
URI:	http://repository.ubharajaya.ac.id/id/eprint/11667

Actions (login required)

View Item

Downloads